Analysis of Mechanical Properties and Permeability of Sand Moulding by Using Eggshell in Sand Casting

Wahyu Kurnianto, Poppy Puspitasari, Wahono Wahono

Abstract


This study aimed to analyse the usage of Eggshell as mixture material of bentonite in metal casting process which used dried sand moulding. Eggshell variations in this study were 4%, 7%, 10% eggshell, and additional 3% of bentonite on each sample. This study used pre-experimental method and included to One-Shot Case Study model. The highest strength was found on the sample 3 ES 10%. Tensile strength of dried sand moulding reach up to 0.09 kg/cm2, the compressive strength of dried sand moulding reached up to 3.11 kg/cm2, and the shear strength of dried sand moulding reached up to 1.13 kg/cm2. Based on the test result indicated that permeability of sand moulding by heat treatment at 110ºC for 60 minutes at sample of 3 ES 10% was at 178.3 ml / min.


Keywords


Mechanical properties, permeability, sand moulding, eggshell.

Full Text:

PDF

References


C. Saikaew dan S. Wiengwiset, “Applied Clay Science Optimization of molding sand composition for quality improvement of iron castings,” Appl. Clay Sci., vol. 67–68, hal. 26–31, 2012.

Andoko, P. Puspitasari, A. A. Permanasari, dan D. Z. Lubis1, “Formula of Moulding Sand, Bentonite and Portland Cement toImprove The Quality of Al-Si Cast Alloy,” J. Mech. Eng. Sci. Technol., vol. 1, no. 2, hal. 49–52, 2017.

F. S. Murakami, P. O. Rodrigues, C. Maria, T. De Campos, M. Antônio, dan S. Silva, “Physicochemical study of CaCO 3 from egg shells,” vol. 27, no. 3, hal. 658–662, 2007.

J. J. Darren, D. Gunaran, H. Hendy, dan E. K. Budirahardjo, “Pengaruh Penambahan Gabungan Batu Kapur the Effect dan Batu Kapur Padam pada Campuran Beton K-300,” hal. 141–148.

M. Multigner, E. Frutos, J. L. González-Carrasco, J. A. Jiménez, P. Marín, dan J. Ibáñez, “Influence of the sandblasting on the subsurface microstructure of 316LVM stainless steel: Implications on the magnetic and mechanical properties,” Mater. Sci. Eng. C, vol. 29, no. 4, hal. 1357–1360, 2009.

W. Yu, H. He, N. Cheng, B. Gan, dan X. Li, “Preparation and experiments for a novel kind of foundry core binder made from modified potato starch,” Mater. Des., vol. 30, no. 1, hal. 210–213, 2009.

N. T. Herwido, P. Murdanto, dan P. Puspitasari, “Analisis Variasi Komposisi Fly Ash Dan Bentonit Pada,” J. Mech. Eng. Sci. Technol., no. 1, hal. 1–11, 2016.

A. Pujianto, A. NA, M. DC, dan Hendra, “Kuat Tekan Beton Geopolimer dengan Bahan Utama bubuk Lumpur lapindo dan Kapur,” Konf. Nas. Tek. Sipil, vol. 7, no. KoNTekS 7, hal. 129–136, 2013.

Anon, “Sand/binders/sand preparation/mold & coremaking,” Foundry Manag. Technol., vol. 124, no. 1, 1996.

M. Holtzer, “The Mold/Casting Interface Phenomena,” in Microstructure and Properties of Ductile Iron and Compacted Graphite Iron Castings: The Effects of Mold Sand/Metal Interface Phenomena, 2015, hal. 77–108.

W. A. Ayoola, S. O. Adeosun, O. S. Sanni, dan A. Oyetunji, “Effect of casting mould on mechanical properties of 6063 aluminum alloy,” J. Eng. Sci. Technol., vol. 7, no. 1, hal. 89–96, 2012.

M. V. Mohiuddin, A. Krishnaiah, dan S. F. Hussainy, “Effect of Composition of Sand Mold on Mechanical Properties and Density of Al-Alloy Casting Using Taguchi Design Approach,” Int. J. Eng. Res. Appl., vol. 5, no. 3, hal. 37–41, 2015.

S. Priyadharsini dan P. Karunakaran, “Determination of the Physical Properties of Sand Moulding Bonded with Composite of Ipomoea Batatas and Bentonite with Casting Application,” hal. 2913–2919, 2016.




DOI: http://dx.doi.org/10.17977/um016v2i22018p079

Refbacks

  • There are currently no refbacks.


Copyright (c) 2018 Journal of Mechanical Engineering Science and Technology

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

View My Stats